Soviet Rubber Technology, Volume 301971 - Rubber industry and trade |
From inside the book
Results 1-3 of 50
Page 5
... monomers in the production of crosslinked rubbers does not normally exceed 75 % ( Refs . 4,5 ) . The results of testing of rubbers of series 3 shows that increasing the monomer conversion from 60 to 95 % causes a considerable increase ...
... monomers in the production of crosslinked rubbers does not normally exceed 75 % ( Refs . 4,5 ) . The results of testing of rubbers of series 3 shows that increasing the monomer conversion from 60 to 95 % causes a considerable increase ...
Page 7
... monomer bonded with. Table 1 Properties of latices with a third monomer Property Type of monomer AN DEAEMA MVP VP MMA 5 parts 10 parts 10 parts 5 parts 5 parts 10 parts 5 parts 10 parts Content of combined VC in the copolymer , % 43 38 ...
... monomer bonded with. Table 1 Properties of latices with a third monomer Property Type of monomer AN DEAEMA MVP VP MMA 5 parts 10 parts 10 parts 5 parts 5 parts 10 parts 5 parts 10 parts Content of combined VC in the copolymer , % 43 38 ...
Page 8
... monomer test Abrasion mm / min Stiffness , kgf / cm2 test control DEAEMA 5 parts 1.48 0.8 10 parts 1.23 0.76 MVP 5 parts 1.45 0.91 10 parts 1.47 0.84 AN 10 parts 1.18 0.83 15 parts 1.29 0.81 VP 10 parts 0.88 0.65 MMA 5 parts 10 parts ...
... monomer test Abrasion mm / min Stiffness , kgf / cm2 test control DEAEMA 5 parts 1.48 0.8 10 parts 1.23 0.76 MVP 5 parts 1.45 0.91 10 parts 1.47 0.84 AN 10 parts 1.18 0.83 15 parts 1.29 0.81 VP 10 parts 0.88 0.65 MMA 5 parts 10 parts ...
Contents
TECHNOLOGY | 1 |
DEPENDENCE OF THE PHYSICAL PROPERTIES OF ELASTOMERS ON THEIR CHEMICAL COMPOSITION | 8 |
RUBBERS OBTAINED BY EMULSION POLYMERISATION METHODS | 15 |
2 other sections not shown
Other editions - View all
Common terms and phrases
addition adhesion amount assessed belt bond break breaker calculated carcass carried chemical coefficient combination components constant containing copolymer cord crosslinking curve deformation density dependence determined developed device effect elastic elongation equation et al experimental factors falls fatigue filler flow force friction gaskets given gives groups heat higher improved increase industry influence initial kgf/cm² latex load lower material maximum measuring medium method MICHIGAN mixer mixes mixes based moulding observed obtained operation P. G. Williams polymer possible presence pressure processing production properties radial range RAPRA ratio Received for publication reduces Research Institute resin resistance respectively Rubb rubber sealing shear shows Soviet specimens speed standard stress structure studied sulphur surface Table temperature tensile strength testing Translated by P. G. tread tyres unit viscosity vulcanisates