Fatigue and Fracture Mechanics: 28th Volume |
Contents
A HISTORICAL PERSPECTIVE | 3 |
EFFECT OF INTERFACIAL CHARACTERISTICS ON MODE I FRACTURE BEHAVIOUR OF GLASS WOVEN FABRIC COMPOSITES UNDER S... | 53 |
APPLICATION OF FRACTURE MECHANICS IN MAINTENANCE OF HIGH TEMPERATURE EQUIPMENT AN ASSESSMENT OF CRITICAL ... | 70 |
ON SPACE FLIGHT PRESSURE VESSEL FRACTURE CONTROL | 86 |
AN XRAY DIFFRACTION STUDY OF MICROSTRUCTURAL DEFORMATION INDUCED BY CYCLIC LOADING OF SELECTED STEELS | 105 |
A NEW EFFECTIVE CRACK GROWTH MODEL | 123 |
FRACTURE TOUGHNESS RESULTS AND PRELIMINARY ANALYSIS FOR INTERNATIONAL COOPERATIVE TEST PROGRAM ON SPECIM... | 146 |
INFLUENCE OF PRESTRAIN ON FRACTURE TOUGHNESS AND STABLE CRACK GROWTH IN LOW CARBON STEELS | 167 |
STRESS CONCENTRATION STRESS INTENSITY AND FATIGUE LIFETIME CALCULATIONS FOR SHRINKFIT COMPOUND TUBES CONTA... | 385 |
FATIGUE ANALYSIS OF A VESSEL EXPERIENCING PRESSURE OSCILLATIONS | 397 |
FATIGUE CRACK GROWTH IN THE HIGHLY PLASTIC REGIME | 411 |
FRACTURE INITIATION BY LOCAL BRITTLE ZONES IN WELDMENTS OF QUENCHED AND TEMPERED STRUCTURAL ALLOY STEEL P... | 427 |
EFFECT OF WELD METAL MISMATCH ON JOINT EFFICIENCY AND MEASURED FRACTURE TOUGHNESS | 450 |
NUMERICAL ANALYSIS AND EXPERIMENTAL VERIFICATION | 469 |
FRACTURE ASSESSMENT OF WELD MATERIAL FROM A FULL THICKNESS CLAD RPV SHELL SEGMENT | 485 |
INCORPORATION OF RESIDUAL STRESS EFFECTS INTO FRACTURE ASSESSMENTS VIA THE FINITE ELEMENT METHOD | 499 |
3D CONSTRAINT EFFECTS ON MODELS FOR TRANSFERABILITY OF CLEAVAGE FRACTURE TOUGHNESS | 179 |
ESTIMATION OF LOWERBOUND KJC ON PRESSURE VESSEL STEELS FROM INVALID DATA | 198 |
FRACTURE OF SURFACE CRACKS LOADED IN BENDING | 214 |
DUCTILETOBRITTLE TRANSITION CHARACTERIZATION USING SURFACE CRACK SPECIMENS LOADED IN COMBINED TENSION AND... | 243 |
APPLICATION OF SMALL SPECIMENS TO FRACTURE MECHANICS CHARACTERIZATION OF IRRADIATED PRESSURE VESSEL STEELS | 263 |
SINGLE SPECIMEN METHOD FOR DETERMINING THE MASTER CURVE IN THE TRANSITION | 280 |
APPLICATION OF JQ THEORY TO THE LOCAL APPROACH STATISTICAL MODEL OF CLEAVAGE FRACTURE | 296 |
ANALYSIS OF STABLE TEARING IN A 76 MM THICK ALUMINUM PLATE ALLOY | 309 |
FATIGUE TECHNOLOGY IN GROUND VEHICLE DESIGN | 326 |
SERVICE LOAD FATIGUE TESTING OF RAILWAY BOGIE COMPONENTS | 342 |
SOME METHODS OF REPRESENTING FATIGUE LIFETIME AS A FUNCTION OF STRESS RANGE AND INITIAL CRACK SIZE | 355 |
DEVELOPMENT OF A RAPID THERMOMECHANICAL FATIGUE TEST METHOD | 370 |
ANALYSIS OF UNCLAD AND SUBCLAD SEMIELLIPTICAL FLAWS IN PRESSURE VESSEL STEELS | 515 |
PREDICTING CRACK INSTABILITY BEHAVIOUR OF BURST TESTS FROM SMALL SPECIMENS FOR IRRADIATED Zr25Nb PRESSURE TU... | 534 |
PREDICTING FRACTURE BEHAVIOR OF ALUMINUM ALLOYS | 562 |
THE EFFECT OF CRACK INSTABILITYSTABILITY ON FRACTURE TOUGHNESS OF BRITTLE MATERIALS | 577 |
HYDROGEN INDUCED CRACKING TESTS OF HIGH STRENGTH STEELS AND NICKELIRON BASE ALLOYS USING THE BOLTLOADED S... | 602 |
COMPUTER SIMULATION OF FAST CRACK PROPAGATION AND ARREST IN STEEL PLATE WITH TEMPERATURE GRADIENT BASED O... | 617 |
STRESS INTENSITY MAGNIFICATION FACTORS FOR FULLY CIRCUMFERENTIAL CRACKS IN VALVE BODIES THICK CYLINDERS | 641 |
K3D A PROGRAM FOR DETERMINING STRESS INTENSITY FACTORS OF SURFACE AND CORNER CRACKS FROM A HOLE | 656 |
FINITE ELEMENT ANALYSIS ON THE FRACTURE OF RUBBER TOUGHENED POLYMER BLENDS | 671 |
AUTHOR INDEX | 685 |
| 687 | |
Other editions - View all
Common terms and phrases
Alloy American Society analysis ASTM International ASTM STP autofrettage behavior bending brittle calculated clad beam cleavage fracture compact specimens components configuration COPV crack depth crack extension crack front crack growth crack initiation crack length crack propagation crack tip critical CTOA CTOD cycles cyclic damage deformation determined displacement ductile elastic elastic-plastic equation evaluated experimental failure Fatigue and Fracture fatigue crack fatigue precrack Figure finite element analysis flaw Fracture Mechanics fracture toughness hole hoop stress J-integral K₁ Kmax laminate linear elastic lower bound master curve maximum measured method microstructural MPa√m Newman notch parameters PCVN specimens plane strain plastic strain plastic zone plate pre-strain predicted pressure vessel ratio region residual stress rubber particle SE(B shown in Fig simulation small-crack Society for Testing steel stress intensity factor stress range structural surface crack tensile tensile stress Testing and Materials thickness toughness values transition tube weld metal yield strength