Welding: Theory and Practice |
From inside the book
Results 1-3 of 12
Page 108
Frank N. Masson. BRAZE - WELDING AND BRAZING FIG . 17 : 2 Effects of shear load . CHAPTER 17 Braze - welding is a bonding process of joining metal at a temperature greater than 800 ° F . but less than the melting- point of the metal to ...
Frank N. Masson. BRAZE - WELDING AND BRAZING FIG . 17 : 2 Effects of shear load . CHAPTER 17 Braze - welding is a bonding process of joining metal at a temperature greater than 800 ° F . but less than the melting- point of the metal to ...
Page 110
... braze - welding it is necessary to keep the heat localized . The filler metal will spread to any section that has been fluxed and heated sufficiently and dis- persed heat will result in too large a weld . The ability to recognize the ...
... braze - welding it is necessary to keep the heat localized . The filler metal will spread to any section that has been fluxed and heated sufficiently and dis- persed heat will result in too large a weld . The ability to recognize the ...
Page 114
... welding , braze - weld- ing , and brazing . 2. What are the three main factors that ensure satisfactory welds in braze- welding ? 3. Why are oxidizing - type fluxes used for braze - welding ? 4. Why is it necessary to round off all ...
... welding , braze - weld- ing , and brazing . 2. What are the three main factors that ensure satisfactory welds in braze- welding ? 3. Why are oxidizing - type fluxes used for braze - welding ? 4. Why is it necessary to round off all ...
Contents
Definition and History of Welding | 1 |
Oxyacetylene Equipment | 15 |
Filler Rods | 29 |
Copyright | |
4 other sections not shown
Common terms and phrases
acetone acety acetylene Acetylene cylinders adjust alloy alternating current amperage amperes arc length base metal Bevel braze-welding brazing Butt Joint cable carbide carbon carburizing flame cast iron cause cent colour connections copper Corner Joint cutting torch diameter Amperage range direct current Direction of Weld duty cycle edge elec electric electrode Electrode angles electrode holder equipment EXERCISE filler metal filler rod fillet welds flame test flat position flow flux furnace gases heat hose hydrogen inner cone iron powder Lap Joint lead angle lene Liquid Air Ltd machine manifold manufactured melt method mild steel molten metal molten pool neutral flame nickel operator oxides Oxidizing Flame oxyacetylene welding pass penetration preheat produce Reduction Company Incorporated regulator shape shield shown in Figure Silver-brazing alloys slag stringer bead sure surface tack welds Tee Joint temperature tion trode type of welding undercut usually voltage weave weld metal welder welding tip welding torch