Acrylic Resins |
From inside the book
Results 1-3 of 29
Page 129
... film may easily be made by some standard film - spreading devices which can be adjusted to the desired film thickness . A piece of plate glass is an excellent base for film casting , but many emulsions adhere to glass and are difficult ...
... film may easily be made by some standard film - spreading devices which can be adjusted to the desired film thickness . A piece of plate glass is an excellent base for film casting , but many emulsions adhere to glass and are difficult ...
Page 130
... films at temperatures normally used in forced drying . The surface glossiness of a film can be measured by a glossmeter which determines the amount of light reflected from the film surface at a particular angle . The usual angle is 60 ...
... films at temperatures normally used in forced drying . The surface glossiness of a film can be measured by a glossmeter which determines the amount of light reflected from the film surface at a particular angle . The usual angle is 60 ...
Page 131
... film , the less the oscillations will change in amplitude during a given time . In a softer material the rocker will sink into the film to some extent and will be going " uphill ” as it rolls back and forth . This will slow up the ...
... film , the less the oscillations will change in amplitude during a given time . In a softer material the rocker will sink into the film to some extent and will be going " uphill ” as it rolls back and forth . This will slow up the ...
Other editions - View all
Acrylic Resins: Reinhold Plastics Applications Series, Issue 14 Milton B. Horn No preview available - 2012 |
Acrylic Resins: Reinhold Plastics Applications Series, Issue 14 Milton B. Horn No preview available - 2012 |
Common terms and phrases
acetate acrolein acrylic acid acrylic and methacrylic acrylic emulsions acrylic esters acrylic fibers acrylic molding acrylic monomers acrylic resins acrylic sheet acrylonitrile addition adhesives agents anionic application benzoyl peroxide blade bond bulk polymerization cast acrylic cast sheet catalyst cell cement cent Chemical coatings color compounds cooling copolymer Copolymerization crazing cross-linking cycles droplets emulsifier emulsion polymerization ethyl acrylate excellent exotherm extruded fabrics factor fibers film finished glass Haas Reporter improve inch inhibitor injection molding lower machine manufacture materials merization methacrylic acid method methyl methacrylate molding powder molecular weight mono monomer nitrile operation optical oven paint paper particle pigment plastic PLEXIGLAS poly polymeriza pressure problem properties range rapidly reaction remove rods Rohm & Haas rubber shrinkage small amount sodium soluble solution polymers solvent strength styrene surface surfactant suspension polymerization synthetic temperature tensile testing textile thickness tion tube vinyl viscosity water-soluble