American amount apparatus bituminous bituminous coal boiler bridge building burner burning cable railway capacity cars cement cement kiln cent combustion Committee Company concrete construction conveyor cost curve cylinder diameter discharge dust efficiency electric equipment fahr firebox Flange furnace gases granolithic grinding handling heating surface heating value hoists horsepower increase industrial installation joint kiln knife edge lever load locomotive machine Manufacturers material Mechanical Engineers method mill Minneapolis moisture municipal North Western Fuel obtained operation paper pipe pitot tube plant police Portland cement powdered coal practice present pressure pulverized coal rail ratio screen screw conveyor sewage shaft slag sludge snow Society speed Standard station load steam steel stoker storage sulphur superheater temperature tests tion tons tube universal joint unloading velocity volatile matter weigh bridge wheel
Page 1017 - The inspector representing the purchaser shall have free entry, at all times while work on the contract of the purchaser is being performed, to all parts of the manufacturer's works which concern the manufacture of the bars ordered.
Page 1015 - Material which shows injurious defects subsequent to its acceptance at the manufacturer's works will be rejected, and the manufacturer shall be notified.
Page 1017 - ... works which concern the manufacture of the bars ordered. The manufacturer shall afford the inspector, free of cost, all reasonable facilities to satisfy him that the bars are being furnished in accordance with these specifications. All tests (except check analyses) and inspection shall be made at the place of manufacture prior to shipment, unless otherwise specified, and shall be so conducted as not to interfere unnecessarily with the operation of the works.
Page 1026 - Section 6, which represent rejected castings, shall be preserved for two weeks from the date of the test report. In case of dissatisfaction with the results of the tests, the manufacturer may make claim for a rehearing within that time.
Page 1021 - ... (b) If any test specimen shows defective machining or develops flaws, it may be discarded and another specimen substituted. (c) If the percentage of elongation of any tension test specimen is less than that specified in Section 5 (a) and any part of the fracture is more than f in.
Page 1021 - Par. 67, and any part of the fracture is more than % in. from the center of the gage length of a 2-in.
Page 1011 - An analysis to determine the percentages of carbon, manganese, phosphorus, and sulphur shall be made by the manufacturer from a test ingot taken during the pouring of each melt, a copy of which shall be given to the purchaser or his representative. This analysis shall conform to the requirements specified in Section 6.
Page 1068 - The safety valve capacity of each boiler shall be such that the safety valve or valves will discharge all the steam that can be generated by the boiler without allowing the pressure to rise more than 6 per cent above the maximum allowable working pressure, or more than 6 per cent above the highest pressure to which any valve is set.