Ceramics of Ancient Persia |
From inside the book
Results 1-3 of 29
Page 21
... yellow , and white . Green glaze was not examined . Analysis of the dark purple glaze shows that iron , man- ganese and titanium compound were used as raw materials to provide the dark color . The blue glaze did not contain lead , but ...
... yellow , and white . Green glaze was not examined . Analysis of the dark purple glaze shows that iron , man- ganese and titanium compound were used as raw materials to provide the dark color . The blue glaze did not contain lead , but ...
Page 24
... yellow triangles . Probably the piece came from the top or bottom border of a large wall picture of colored glazed bricks . The outlines of the patterns on this brick are trimmed with dark purple glaze . It appears that a squeezing ...
... yellow triangles . Probably the piece came from the top or bottom border of a large wall picture of colored glazed bricks . The outlines of the patterns on this brick are trimmed with dark purple glaze . It appears that a squeezing ...
Page 26
... yellow glaze is antimony oxide , and titanium oxide is a supplementary material . It is a lead glaze , of the same kind as the yellow glaze used on the early glazed ceramics made in the Azerbaijan region . Hardly any fluxing agent such ...
... yellow glaze is antimony oxide , and titanium oxide is a supplementary material . It is a lead glaze , of the same kind as the yellow glaze used on the early glazed ceramics made in the Azerbaijan region . Hardly any fluxing agent such ...
Contents
Emergence of Glaze in the Elam Kingdom | 3 |
The Achaemenid Dynasty | 22 |
The Parthian Dynasty | 28 |
Copyright | |
2 other sections not shown
Common terms and phrases
1st-3rd century A.D. 9th century B.C. Achaemenid dynasty Azerbaijan Azerbaijan region band blue glaze body bottom Calcium oxide century B.C. Height CHEMICAL ANALYSIS Chemical Percentage Formula Clay colored glazed brick Compound Chemical Percentage covered with blue Cupric oxide cylindrical jar dark purple decorative applied patterns Dura-Europos East Berlin Faience Ferric oxide Ferric oxide Fe2O3 glazed ceramics Glazed jar green Green-glazed jar Haft Tepe handles and decorative Hasanlu Height including lid horizontal Hyōgo inside Iran Iranian highlands jar with decorative jar with three Kōjirō Ishiguro lead glaze lotus pattern Mesopotamia mouth neck Okayama pair of handles Parthian Percentage Formula Content piece shown Potassium oxide K₂O pottery Private collection rhyton rim diameter Sassanian period Seleucia shoulder shown in plate Silica SiO2 Siraf Sodium oxide surface Susa Tchoga Zanbil Tepe three handles Titanium dioxide Tokyo triangular patterns unearthed from Susa vertical vessel Vicinity of Ziwiye white glaze yellow glaze